PROPERTIES(1)
　
Property Table for Laminates used for Hot Punching
Test items Designations SD-100H SD-1000
NEMA/JIS Grade XP (X)
Unit Condition(2) PL-PEM-P PL-PM
PHYSICAL
Specific Gravity - A 1.30-1.45 1.30-1.45
Heat Resistance,
2 hr		 ℃ A 120 120
Water Absorption(3) % E-24/50+D24/23 2.00 1.50
CHEMICAL
Resistance to Acetone - A - No Change
Flame Classification,
UL-94		 - C-48/23/50+E-168/70 94HB 94HB
ELECTRICAL
Withstand Voltage,
Flatwise		 kV/mm C-90/20/65 13-18 -
Withstand Voltage,
Edgewise		 kV O-0.5/90 8-10 -
Insulation Resistance MΩ C-90/20/65 5x102-5x104 -
Insulation Resistance,
after boiling		 MΩ C-90/20/65+D-2/100 5-100 -
Volume Resistivity MΩ-cm C-90/20/65 102-104 102-103
Surface Resistivity MΩ C-90/20/65 102-104 10-102
Permittivity
(1MHz)		 C2/N‧m2 C-90/20/65 - -
Loss Tangent
(1MHz)		 - C-90/20/65 - -
MECHANICAL
Flexural Strength,
perpendicular		 Kgf/mm2 A 8.0-15.0 11.0-17.0
Izod
Impact Strength,
parallel		 Kgf-cm/cm A 3.0-18.0 3.0-20.0
Bonding Strength Kgf A 350-450 350-450
Compressive Strength,
perpendicular		 Kgf/mm2 A - -
Compressive Strength,
parallel		 Kgf/mm2 A - -
Hardness,
Shore D		 ° A 90-92 90-92
　
　
　
Property Table for Laminates used for Cold Punching
Test items Designations SD-102C SD-168C SD-VR SDF-600C SDF-668C
NEMA/JIS Grade (XPC) XPC (XXXPC) (FR-2) FR-2
Unit Condition(2) PL-PEM-P PL-PEM-P PL-PES-P PL-PES-PF PL-PES-PF
PHYSICAL
Specific Gravity - A 1.30-1.45 1.30-1.45 1.25-1.40 1.35-1.50 1.35-1.50
Heat Resistance
2 hr		 ℃ A 120 120 120 120 120
Water Absorption(3) % E-24/50+D24/23 2.00 2.50 1.20 1.50 1.50
CHEMICAL
Resistance to Acetone - A - - - - -
Flame Classification,
UL-94		 - C-48/23/50+E-168/70 94HB 94HB 94HB 94V-0 94V-0
ELECTRICAL
Withstand Voltage,
Flatwise		 kV/mm C-90/20/65 14-21 14-19 - 13-17 13-17
Withstand Voltage,
Edgewise		 kV O-0.5/90 - - - - -
Insulation Resistance MΩ C-90/20/65 5x102-5x104 5x102-5x104 103-106 103-106 103-106
Insulation Resistance,
after boiling		 MΩ C-90/20/65+D-2/100 5-500 5-500 20-3000 20-1000 20-1000
Volume Resistivity MΩ-cm C-90/20/65 103-105 105-107 106-107 105-107 105-107
Surface Resistivity MΩ C-90/20/65 103-105 105-107 106-107 104-106 104-106
Permittivity
(1MHz)		 C2/N‧m2 C-90/20/65 - - 4.0-5.5 4.0-5.5 4.0-5.5
Loss Tangent
(1MHz)		 - C-90/20/65 - - 0.03-0.05 0.03-0.05 0.03-0.05
MECHANICAL
Flexural Strength,
perpendicular		 Kgf/mm2 A 8.0-10.0 8.0-13.0 8.0-10.0 8.0-14.0 8.0-14.0
Izod
Impact Strength,
parallel		 Kgf-cm/cm A - - - - -
Bonding Strength Kgf A - - - - -
Compressive Strength,
perpendicular		 Kgf/mm2 A - - - - -
Compressive Strength,
parallel		 Kgf/mm2 A - - - - -
Hardness,
Shore D		 ° A 86-88 88-90 86-88 87-89 87-89
　
　
　
Property Table for Fabric-based Laminates
Test items Designations SDL-4060 SDC-5050
NEMA/JIS Grade (LE) (C)
Unit Condition(2) PL-FLE PL-FCM
PHYSICAL
Specific Gravity - A 1.30-1.45 1.30-1.45
Heat Resistance
2 hr		 ℃ A 140 140
Water Absorption(3) % E-24/50+D24/23 2.30 1.50
CHEMICAL
Resistance to Acetone - A No Change No Change
Flame Classification,
UL-94		 - C-48/23/50+E-168/70 94HB 94HB
ELECTRICAL
Withstand Voltage,
Flatwise		 kV/mm C-90/20/65 10-20 10-18
Withstand Voltage,
Edgewise		 kV O-0.5/90 - -
Insulation Resistance MΩ C-90/20/65 103-105 50-100
Insulation Resistance,
after boiling		 MΩ C-90/20/65+D-2/100 30-3000 1-20
Volume Resistivity MΩ-cm C-90/20/65 103-105 1-102
Surface Resistivity MΩ C-90/20/65 103-105 1-102
Permittivity
(1MHz)		 C2/N‧m2 C-90/20/65 - -
Loss Tangent
(1MHz)		 - C-90/20/65 - -
MECHANICAL
Flexural Strength,
perpendicular		 Kgf/mm2 A 8.0-11.0 8.5-11.0
Izod
Impact Strength,
parallel		 Kgf-cm/cm A 4.0-16.0 12.0-28.0
Bonding Strength Kgf A 450-550 550-650
Compressive Strength,
perpendicular		 Kgf/mm2 A - 20-28
Compressive Strength,
parallel		 Kgf/mm2 A - 14-19
Hardness,
Shore D		 ° A 90-92 90-92
　
Notes:
(1) Testing methods are according to JIS-K6911, JIS-K7215 and UL94.
　
(2) The alphabet in condition indicates the kind of conditioning of specimen.
　
A: as received without conditioning.
C: conditioned in air under constant temperature and humidity.
D: immersed in water under constant temperature.
E: conditioned in air under constant temperature.
O: immersed in oil under constant temperature.
　
The first figure is the conditioning time(hours),the second figure is the conditioning temperature(℃) and the third figure is the conditioning relative humidity(%).　
(3) Water absorption test was sampled with products thickness at 1.5mm, except for SD-1000, SD-2000, SDL-4050, SDC-5050, SDC-5055, the test was done at products thickness of 8.0mm.

　
　